SSC-410NiMo/E410NiMoT1-1

SSC-410NiMo													Classifications: GB/T17853 TS 410NiMo-F C1 1 AWS A5.22 E410NiMoT1-1 AWS A5.22M E410NiMoT1-1 EN ISO 17633-A:T 13 4 P C1 1 EN ISO 17633-B:TS 410NiMo-F C1 1
Flux Cored Wire For Stainless Steel
Martensite Type For wear resistance steel
Application:
Suitable for welding in wear resistance steel that has tougher requirements, such as hydraulic turbine rotor, valve, and etc.
Characteristics:
1. With added Ni and Mo, has more stable corrosion resistance, higher hardness and high temperature wear resisance, and can prevent cold crack from happening; 2. Soft and stable arc, few spatter, beautiful weld bead appearance, easy slag removal, smooth feeding,and excellent weldability.
Polarity:
DC+
Welding Position:
Typical Chemical Composition of Weld Metal:
Alloy wt%			C		Mn		Si		Cr		Ni		Mo		P		S		Cu
AWS			0.06		1.0		1.00		11.0-12.5		4.0-5.0		0.4-0.7		0.040		0.030		0.75
SSC-410NiMo			0.030		0.27		0.33		11.35		4.78		0.49		0.015		0.005		0.01
Typical Mechanical Properties of Weld Metal:
Mechanica properties				Y.S.(MPa)			T.S.(MPa)				EI(%)			CVN(J/℃)			PWHT(℃xh)
AWS				-			760				15			-			-
SSC-410NiMo				-			885				17			-			-
Sizes Available and Recommended Parameters:
Dia/mm						1.2					1.4					1.6
Volt						22-36					-					26-38
Amp						120-260					-					200-300
Stick-Out (mm)						15-20					-					18-25
Gas Flow (I/min)						15-25					-					15-25
Notes on usage:
1. Shielding gas: CO₂; 2. Interpass temperature: 150~250℃; 3. Need to perform PWHT at 590~620℃×1hr, air cooling until room temperature.