TIG-2594/ER2594

TIG-2594																	Классификации: YB/T5092 H022Cr25Ni9Mo4N AWS A5.9 ER2594 AWS A5.9M ER2594 ENISO14343-A:G(25 9 4 N L) ENISO14343-B:SS2594
Solid TIG rod for stainless steel
(Austenitic-Ferritic Duplex Alloy)
Применение:
Suitable for welding in offshore engineering, mostly used for UNS S32750, UNS J93380 super duplex stainless steel, often used for root pass welding for duplex stainless steel tube in UNS S32205,J92205.
Характеристики:
1. Nominalcomposition of25.5%Cr-9%Ni-3%Mo-N; 2. Deposited metal has pitting resistance equivalent numbers PREN>=40, thus having excellent pitting resistance, crevice corrosion resistance and stress corrosion resistance; 3. Soft and stable arc, beautiful weld bead appearance, great iron water fluidity, and excellent weldability.
Полярность:
DC-
Положение сварки:
Типичное химическое составление сварного металла:
Сплав wt%			C		Mn		Si		Cr		Ni		Mo		N		P		S		Cu
YB/T			0.03		2.5		1.0		24.0-27.0		8.0-10.5		2.5-4.5		0.2-0.3		0.03		0.02		1.5
AWS			0.03		2.5		1.0		24.0-27.0		8.0-10.5		2.5-4.5		0.2-0.3		0.03		0.02		1.5
Пример			0.016		0.66		0.45		25.27		9.24		3.68		0.24		0.018		0.001		0.06
Типичные механические свойства сварного металла:
Mechanica properties				Y.S.(MPa)			T.S.(MPa)				EI(%)			CVN(J/℃)					FN
YB/T				-			-				-			-					-
AWS				-			-				-			-					-
Пример				-			855				30			240/-40					49
Размеры, доступные и рекомендуемые параметры:
Диаметр/mm						0.8					1.0							1.2
Current Amp			E.H			70-150					100-200							140-220
			OH.V			50-120					80-150							120-180
Замечания по использованию:
1. Shielding gas: 100% Ar; 2.Tungsten stick-out relative to nozzle should be 5mm, arc length should be 1-3mm; 3. Interpass temperature: ≤100℃;