MIG-NiCr3/ERNiCr-3

MIG-NiCr3																	Классификации: GB/T15620 SNi6082 AWS A5.14 ERNiCr-3 AWS A5.14M ERNiCr-3 ISO 18274:S Ni 6082
MIG solid wire for nickel alloy
NiCrType / For Inconel 600
Применение:
1.Suitable for welding Ni-Cr-Fe alloy, such as ASTM B163, B166, B167, B168 and UNS NO6600; 2. Can be used for welding at the side of the layer for Ni-Cr-Fe composite steel, can also be used for buildup welding and dissimilar metal welding.
Характеристики:
1. Nominal compositionis: 72%Ni-20%Cr-3%Mn-2.5%Nb+Ta, Ni-Cr type wire; 2. Deposited metal with excellent mechanical properties and pitting resistance and crevice corrosive resistance; 3. Smooth feeding, stable arc, beautiful weld bead appearance, great iron water fluidity, easy slag removal, excellent weldability.
Полярность:
DC+
Положение сварки:
Типичное химическое составление сварного металла:
Сплав wt%			C		Mn		Si		Cr		Ni		Mo		Fe		Nb-Ta		P		S
GB/T			0.10		2.5-3.5		0.5		18.0-22.0		≥67		-		3.0		2.0-3.0		-		-
AWS			0.10		2.5-3.5		0.5		18.0-22.0		≥67		-		3.0		2.0-3.0		0.030		0.015
Пример			0.024		2.80		0.10		20.3		72		0.17		0.82		2.45		0.002		0.004
Типичные механические свойства сварного металла:
Mechanica properties				Y.S.(MPa)			T.S.(MPa)				EI(%)			CVN(J/℃)					FN
YB/T				-			-				-			-					-
AWS				-			550				-			-					-
Пример				-			670				40			100/-196					-
Замечания по использованию:
1. Shielding gas: Pure Ar, Ar+He or Ar+O₂; 2. Preheat and interpass temperature: <=100℃, and reduce the heat input as much as possible. The Above recommendation is for vour references only, actual operation depends on the environment onsite; set up specific welding procedure after performing a welding process qualification if necessary.