TIG-308LT/ER308LT

TIG-308LT													Классификации: YB/T5092 H022Cr21Ni10 AWS A5.9 ER308L AWS A5.9M ER308L ENISO14343-A: W 19 9 L ENISO14343-B: SS308L JIS Z3321 YS308L
Stainless Steel TIG Solid Wire
Austenitic Alloy For Super Low Temperature
Утверждено:
ABS, BV, CCS, DNV/GL, LR
Применение:
Suitable for welding of 18Cr-8Ni type of low carbon stainless steel, used in petrochemical industry, pressure vessel, food processing equipment, and medicalequipment.
Характеристики:
1. Nominalcomposition is 20%Cr-9%Ni; 2. Deposit meta has excellent mechanica properties and corrosion resistance, also has excellent -196℃ impact toughness; 3. Stable arc, beautiful weld bead appearance, great iron water fluidity, and excellent weldability.
Полярность:
DC-
Положение сварки:
Типичное химическое составление сварного металла:
Сплав wt%			C		Mn		Si		Cr		Ni		Mo		P		S		Cu
YB/T			0.03		1.0-2.5		0.65		19.5-22.0		9.0-11.0		0.75		0.03		0.030		0.75
AWS			0.03		1.0-2.5		0.30-0.65		19.5-22.0		9.0-11.0		0.75		0.03		0.030		0.75
Пример			0.016		1.95		0.54		19.82		9.84		0.01		0.015		0.007		0.01
Типичные механические свойства сварного металла:
Mechanica properties				Y.S.(MPa)			T.S.(MPa)				EI(%)			CVN(J/℃)			PWHT(℃xh)
YB/T				-			-				-			-			-
AWS				-			-				-			-			-
Пример				-			590				41			70/-196			-
Замечания по использованию:
1. Shielding gas: 100% Ar; 2.Shielding gas flow rate: 10-15 l/min; 3. Arc length should be kept between 1-3 mm; 4.Interpass temperature: ≤150℃; 5. Prior to welding, base metal surfaces should be cleaned of grease, oil and corrosion contamination; 6. Take proper protection against wind to prevent blowholes when welding outdoors.