MIG-309LSi/ER309LSi

MIG-309LSi													Классификации: YB/T5092 H022Cr24Ni13S AWS A5.9 ER309LSi AWS A5.9M ER309LSi ENISO14343-A:G 23 12 L Si ENISO14343-B:SS309LSi JIS Z3321 YS309LSi
Stainless Steel MIG Solid Wire
Austenitic Alloy Dissimilar Metal Welding
Утверждено:
DB, CE, JIS
Применение:
For joining carbon or low-alloy steels to stainless steels as well as for welding martensitic and ferritic stainless steels used in petrochemical facilities, thermal power plants and other industries.
Характеристики:
1. Weld deposits have excellent mechanical properties and high corrosion resistance; 2. Improved wash and wetting behavior due to increased content of silicon, stable arc, less spattering, good bead appearance.
Полярность:
DC+
Положение сварки:
Типичное химическое составление сварного металла:
Сплав wt%			C		Mn		Si		Cr		Ni		Mo		P		S		Cu
YB/T			0.03		1.0-2.5		0.65-1.00		23.0-25.0		12.0-14.0		0.75		0.03		0.030		0.75
AWS			0.03		1.0-2.5		0.65-1.00		23.0-25.0		12.0-14.0		0.75		0.03		0.030		0.75
Пример			0.017		1.84		0.87		23.71		13.34		0.01		0.021		0.007		0.05
Типичные механические свойства сварного металла:
Mechanica properties				Y.S.(MPa)			T.S.(MPa)				EI(%)			CVN(J/℃)			PWHT(℃xh)
YB/T				-			-				-			-			-
AWS				-			-				-			-			-
Пример				-			620				35			95/-40			-
Размеры, доступные и рекомендуемые параметры:
Диаметр/mm						0.8					1.0					1.2
Current Amp			E.H			70-150					100-200					140-220
			OH.V			50-120					80-150					120-180
Замечания по использованию:
1. Shielding gas: 98% Ar + 2% O₂; 2.Shielding gas flow rate: 20-25 l/min; 3.Wire stick-out: 15-25 mm; 4. Interpass temperature: ≤150℃; 5. Prior to welding, base metal surfaces should be cleaned of grease, oil and corrosion contamination; 6. Take proper protection against wind to prevent blowholes when welding outdoors.