MIG-309L/ER309L

MIG-309L													Классификации: YB/T5092 H022Cr24Ni13 AWS A5.9 ER309L AWS A5.9M ER309L EN ISO 14343-A:G 23 12 ENISO 14343-B:SS309L JIS Z3321 YS309L
Stainless Steel MIG Solid Wire
Austenitic Alloy Dissimilar Metal Welding
Утверждено:
DB, CE, JIS
Применение:
For joining carbon or low-alloy steels to stainless steels as well as for welding martensitic and ferritic stainless steels used in petrochemical facilities, thermal power plants and other industries. Suitable for the firstlayer cladding of carbon steels.
Характеристики:
1. Weld deposits have excellent mechanical properties and high corrosion resistance; 2. Excellent wire feedability, stable arc, less spattering, good bead appearance.
Полярность:
DC+
Положение сварки:
Типичное химическое составление сварного металла:
Сплав wt%			C		Mn		Si		Cr		Ni		Mo		P		S		Cu
YB/T			0.03		1.0-2.5		0.65		23.0-25.0		12.0-14.0		0.75		0.03		0.030		0.75
AWS			0.03		1.0-2.5		0.65		23.0-25.0		12.0-14.0		0.75		0.03		0.030		0.75
Пример			0.022		2.20		0.57		23.28		13.46		0.01		0.018		0.006		0.04
Типичные механические свойства сварного металла:
Mechanica properties				Y.S.(MPa)			T.S.(MPa)				EI(%)			CVN(J/℃)			PWHT(℃xh)
YB/T				-			-				-			-			-
AWS				-			-				-			-			-
Пример				-			585				39			83/-60			-
Размеры, доступные и рекомендуемые параметры:
Диаметр/mm						0.8					1.0					1.2
Current Amp			E.H			70-150					100-200					140-220
			OH.V			50-120					80-150					120-180
Замечания по использованию:
1. Shielding gas: 98% Ar + 2% O₂; 2.Shielding gas flow rate: 20-25 l/min; 3.Wire stick-out: 15-25 mm; 4. Interpass temperature: ≤150℃; 5. Prior to welding, base metal surfaces should be cleaned of grease, oil and corrosion contamination; 6. Take proper protection against wind to prevent blowholes when welding outdoors.