MIG-308L/ER308L

MIG-308													Классификации: YB/T5092 H022Cr21Ni10 AWS A5.9 ER308L AWS A5.9M ER308L EN ISO14343-A:G 19 9 ENISO14343-B:SS308L JIS Z3321 YS308L
MIG Solid Wire for Stainless Steel
Austenitic Type
Применение:
Suitable for welding 18Cr-8Ni grade low carbon austenitic stainless steels used in petrochemical industry, pressure vessel, food processing equipment, medical equipment, and etc.
Характеристики:
1. Deposited metal have excellent mechanical properties and high corrosion resistance; 2. Smooth feeding, stable arc, beautiful weld bead appearance, great iron water fluidity, few spatter, excellent weldability.
Полярность:
DC+
Положение сварки:
Типичное химическое составление сварного металла:
Сплав wt%			C		Mn		Si		Cr		Ni		Mo		P		S		Cu
YB/T			0.03		1.0-2.5		0.65		19.5-22.0		9.0-11.0		0.75		0.03		0.030		0.75
AWS			0.03		1.0-2.5		0.65		19.5-22.0		9.0-11.0		0.75		0.03		0.030		0.75
Пример			0.018		2.0		0.55		20.1		10		0.01		0.024		0.010		0.02
Типичные механические свойства сварного металла:
Mechanica properties				Y.S.(MPa)			T.S.(MPa)				EI(%)			CVN(J/℃)			PWHT(℃xh)
YB/T				-			-				-			-			-
AWS				-			-				-			-			-
Пример				-			590				39			100/-60			-
Размеры, доступные и рекомендуемые параметры:
Диаметр/mm						0.8					1.0					1.2
Current Amp			E.H			70-150					100-200					140-220
			OH.V			50-120					80-150					120-180
Замечания по использованию:
1. Shielding gas: 98% Ar + 2% O₂; 2. Interpass temperature: ≤150℃; 3. Please follow the processing abstract for stainless steel solid wire in P182.